Application: | Communication |
---|---|
Type: | Single-mode Fiber |
Material Shape: | Round Wire |
Allowed Lateral Pressure: | >1000(N/100mm) |
Allowed Tensile Strength: | 100N<1000N |
Core: | Single Core |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Characteristics | Conditions | Specified values | Units | ||
Optical Characteristics | |||||
Attenuation Attenuation |
1310nm | ≤0.32 | [dB/km] | ||
1383nm(after H2-aging) | ≤0.31 | [dB/km] | |||
1550nm | ≤0.18 | [dB/km] | |||
1625nm | ≤0.20 | [dB/km] | |||
Attenuation vs. Wavelength Max. α difference |
1285-1330nm, in reference to 1310nm | ≤0.03 | [dB/km] | ||
1525-1575nm, in reference to 1550nm | ≤0.02 | [dB/km] | |||
Dispersion Coefficient |
1285-1340nm | -3.5 to 3.5 | [ps/(nm·km)] | ||
1550nm | ≤18 | [ps/(nm·km)] | |||
1625nm | ≤22 | [ps/(nm·km)] | |||
Zero Dispersion Wavelength(λ0) | -- | 1300-1324 | [nm] | ||
Zero Dispersion Slope(S0) | -- | ≤0.092 | [ps/(nm2·km)] | ||
Typical Value | -- | 0.086 | [ps/(nm2·km] | ||
PMD | Maximum Individual Fibre | -- | ≤0.1 | [ps/√km] | |
Link Design Value(M=20,Q=0.01%) | -- | ≤0.06 | [ps/√km] | ||
Typical Value | -- | 0.04 | [ps/√km] | ||
Cable Cutoff Wavelength (λCC) | -- | ≤1260 | [nm] | ||
Mode Field Diameter(MFD) | 1310nm | 8.7-9.5 | [μm] | ||
1550nm | 9.8-10.8 | [μm] | |||
Effective Group Index of Refraction(Neff ) | 1310nm | 1.466 | -- | ||
1550nm | 1.467 | -- | |||
Point Discontinuities | 1310nm | ≤0.05 | [dB] | ||
1550nm | ≤0.05 | [dB] | |||
Geometrical Characteristics | |||||
Cladding Diameter | -- | 125.0±0.7 | [μm] | ||
Cladding Non-Circularity | -- | ≤1.0 | [%] | ||
Coating Diameter | -- | 235-250 | [μm] | ||
Coating-Cladding Concentricity Error | -- | ≤12.0 | [μm] | ||
Coating Non-Circularity | -- | ≤6.0 | [%] | ||
Core-Cladding Concentricity Error | -- | ≤0.6 | [μm] | ||
Curl(radius) | -- | ≥4 | [m] | ||
Delivery Length | -- | Up to 50.4 | [km/reel] | ||
Environmental Characteristics | 1310nm, 1550nm & 1625nm | ||||
Temperature Dependence Induced Attenuation | -60ºC to +85ºC | ≤0.05 | [dB/km] | ||
Temperature-Humidity Cycling Induced Attenuation | -10°C to +85°C, 98% RH | ≤0.05 | [dB/km] | ||
Water Immersion Dependence Induced Attenuation | 23°C,for 30 days | ≤0.05 | [dB/km] | ||
Damp Heat Dependence Induced Attenuation | 85°C and 85% RH,for 30 days | ≤0.05 | [dB/km] | ||
Dry Heat Aging | 85ºC, for 30 days | ≤0.05 | [dB/km] | ||
Mechanical Specifications | |||||
Proof Test |
-- | ≥9.0 | [N] | ||
-- | ≥1.0 | [%] | |||
-- | ≥100 | [kpsi] | |||
Macro-bend Induced Attenuation | 100 Turns Around a Mandrel of 30 mm Radius | 1625nm | ≤0.05 | [dB] | |
100 Turns Around a Mandrel of 25 mm Radius | 1310nm and 1550nm | ≤0.05 | [dB] | ||
1 Turn Around a Mandrel of 16 mm Radius | 1550nm | ≤0.05 | [dB] | ||
Coating Strip Force | typical average force | 1.5 | [N] | ||
peak force | 1.3-8.9 | [N] | |||
Dynamic Fatigue Parameter(nd) | -- | ≥20 | -- |
Suppliers with verified business licenses