Fiber Specifications |
Main Indexes |
Technical Parameter |
- Dimensions
Specifications |
Cladding Diameter |
125.0±1.0 um |
Cladding non-circularity |
≤1 % |
Coating diameter |
245±10 um |
Coating/cladding concentricity |
≤12 um |
Coating Non-Circularity |
≤6 % |
Core/Cladding Concentricity |
≤0.6 um |
Fiber Curl (radius) |
≥4 m |
Fiber Lengths |
2.1-24.45 km/spool |
- Optical
Specifications |
Mode-Field Diameter (MFD) |
1310nm |
9.2±0.4 um |
1550nm |
10.4±0.6 um |
Attenuation |
1310nm |
≤0.36 dB / km |
1550nm |
≤0.22 dB / km |
1625nm |
≤0.24 dB / km |
Attenuation VS. Wavelength |
@1285-1330nm, Ref. λ@1310nm |
≤0.04 dB / km |
@1525-1575nm, Ref. λ@1550nm |
≤0.03 dB / km |
Point Discontinuity |
1310nm |
≤0.05 dB |
1550nm |
≤0.05 dB |
Polarization Mode Dispersion(PMD) |
Maximum individual fiber (PMD) |
≤0.2 ps/(km1/2) |
PMD link design value(M=20,Q=0.01%) |
≤0.1 ps/(km1/2) |
Typical value |
0.04 ps/(km1/2) |
Zero Dispersion Wavelength(λ0) |
1312±12 nm |
Zero Dispersion Slope(S0) |
≤0.091 ps/(nm2.km) |
Dispersion in the range of wavelength |
1285~1339nm |
≤3.4 ps/(nm.km) |
1271~1360nm |
≤5.3 ps/(nm.km) |
Cable cutoff wavelength λcc |
≤1260nm |
- Mechanical Specifications
|
Proof test |
≥9.0N, ≥1.0%, ≥100Kpsi |
Dynamic stress corrosion susceptibility parameters (Nd) |
≥20 |
Coating strip force |
Average value |
1.5N |
Peak |
1.3-8.9N |
Macrobend loss |
1turn Φ32mm, 1550nm |
≤0.05 dB |
100 turns Φ50mm, 1310nm&1550nm |
≤0.05 dB |
100 turns Φ60mm, 1625nm |
≤0.1 dB |
- Environmental Specifications
|
Temperature dependence(-60ºC to +85ºC, 1550nm&1625nm) |
≤0.05 dB / km |
Temperature humidity cycling(-10ºC to ±85ºC, at 98%RH, 1550nm&1625nm) |
≤0.05 dB / km |
Water immersion(23±2ºC, 30 days, 1550nm&1625nm) |
≤0.05 dB / km |
Dry Heat Soak(85±2ºC, 30 days, 1550nm&1625nm) |
≤0.05 dB / km |
Damp Heat(85±2ºC at 85%RH, 1550nm&1625nm) |
≤0.05 dB / km |